材質表 > > |
Table: I Type | Bronze | Brass | Fe | Fe-Cu | Fe-C | Fe-Cu-C | Fe-Cu-Ni-C | Cu Infiltrate | MPIF Standard | CT-1000 | CZP-2002 | F-0000 | - | F-0008 | FC-0205 | FD-0205 | FD-0405 | FX-1008 | JIS Standard | SBK 1218 | - | SMF 1015 | SBF 2218 | SMF 3020 | SMF 4030 | SMF 5030 | SMF 5040 | - | Heat Trement | - | - | - | - | • | • | • | • | • | Chemical Composition
(%) | Fe | - | - | bal | bal | bal | bal | bal | bal | bal | C | - | - | - | - | 0.4~0.8 | 0.3~0.6 | 0.3~0.6 | 0.3~0.6 | 0.3~0.8 | Cu | bal | 77~88 | - | 18~25 | 1~3 | 1~3 | 1~2.5 | 1~2.5 | 8~6 | Sn | 8~11 | - | - | - | - | - | - | - | - | Ni | - | - | - | - | - | - | 1~3 | 3~5 | - | Pb | - | 1~2 | - | - | - | - | - | - | - | Zn | - | bal | - | - | - | - | - | - | - | Mo | - | - | - | - | - | - | 0.5 | 0.5 | - | Others | < 1.0 | < 1.0 | < 1.0 | < 1.0 | < 1.0 | < 1.0 | < 1.0 | < 1.0 | < 4.0 | Physial Mechanical Properties | Density
(g/cm3) | 6.4~6.8 | 7.6~8.0 | 6.8 Min | 5.6~6.4 | 6.2~6.8 | 6.2~6.8 | 6.6~6.8 | 6.8 Min | 7.2 Min | Oil Content
(VOL. %) | 18 Min | - | - | 18 Min | - | - | - | - | - | Ultimate Tensile Strength
(kg/mm2) | 8 | 15 | 20 | 15 | 30 | 50 | 40 | 40 | 60 | Elongation (%) | 2 | 10 | 5 | 1.0 | 0.5 | 1.0 | 1.0 | 1.0 | 2.0 | Radial Crushing Strength
(kg/mm2) | 15 Min | - | - | 20 Min | - | - | - | - | - | Hardness | RH
30~70 | RH
75 | RB
20 | RH
30~70 | RB
40 | RB
40 | RB
60 | RB
70 | RB
80 |
Table:II Type | Chemical Composition (%) | Physial Mechanical Properties | Fe | Cr | Ni | Cu | Tin | Si | Mn | Mo | C | S | Others | Density
(g/cm3) | Ultimate Tensile Strength
(kg/mm2) | Elongation
(%) | Hardness | SS-303L | bal | 18.2 | 12.5 | 2.0 | 1.0 | 0.8 | 0.13 | - | <0.08 | 0.02 | <1.0 | >6.3 | >20 | >2.0 | RB40 | SS-304L | bal | 18.3 | 10.9 | - | 1.0 | 0.9 | 0.13 | - | <0.08 | 0.02 | <1.0 | >6.3 | >20 | >2.0 | RB40 | SS-316L | bal | 17.0 | 13.5 | 2.0 | 1.0 | 0.75 | 0.12 | 2.2 | <0.08 | 0.01 | <1.0 | >6.3 | >25 | >5.0 | RB38 | SS-410L | bal | 12.8 | - | - | - | 0.8 | 0.17 | - | <0.08 | 0.01 | <1.0 | >6.3 | >20 | >2.0 | RB80 |
|
|
|
|
|